The concrete sealer is a proprietary blend of reactive silicates, which penetrates into the concrete and reacts with the free calcium and lime to form an insoluble by-product that closes the porosity, increases the mass, strengthens, hardens and seals the concrete, makes it much more durable and resistant to damage by chemicals and mechanical abrasion. The sealer can be used on bridge decks, loading ramps, driveways, runways, fueling stations, and farms to increase the life of concrete infrastructures. The sealer is the only reactive silicate product in the world that meets both the Illinois & Ohio DOT’s specification for use on bridge structures and decks.
The application process is non-toxic, non-hazardous, and non-flammable. There are no special handling requirements under environmental regulations and contains ZERO VOC content.
The sealer can be applied in temperatures up to 95º F and as low as 38º F. Concrete must NOT be allowed to freeze for 24 hours after application. DO NOT ALLOW THIS PRODUCT TO FREEZE. DO NOT APPLY TO WET CONCRETE SURFACES. Clean up with soap and water immediately after use. CAUTION: Leaving residue in spraying equipment may damage equipment.
Drying time is 4 hours and reaches full cure in about 75 days. Surface can be used as soon as it is completely dry. Do not get surface wet for 12 hours.
SYNOPSIS OF LAB TEST:
ASTM C-672 / 666 NO SCALING / see airport report
Cycles 100 with calcium chloride solution
Absorption Less than 1% after 48 hours / Less than 2% after 50 days.
AASHTO T 259 Modified Crack sealing capability Per-ODOT Spec. 841 Passed.
Chloride Absorption Specimen#1= 0.081% Specimen #2=0.056%
Dry Time
To Touch 4 hrs
Dry Hard 12 hrs
Color Clear
Specific Gravity (H20 = 1) 1.04
VOC, grams / liter 0
pounds / gallon 0
Abrasion Resistance Treated vs Non-Treated Specimen ASTM C-779
Continuous rotating grinding disk under pressure for 60 minuets.
Abrasion Resistance Increase @ 30 minutes 45% wear in. 0.044 vs 0.080